We are very much interested to have business relations with you. We foresee very good potential business opportunities for your products with the present oil & gas sector and demand would be increasing due to the up-coming projects in various areas. We are very confident and capable to promote your products in a professional way with our professionally managed team and sound technical knowledge.
In this regard, please note that we have been requested to quote for the following Refractory Fire Bricks. Please find below the technical specifications for your review and quote.
Appreciate receiving your CIF Kuwait offer.
|
Line # |
Item # |
Description |
Qty |
Units |
|
1 |
038231 |
REFRACTORY:FORM FIREBRICK INSULATING,9 IN WD X 13-1/4 IN LG X 3 IN THK |
360 |
EACH |
|
Description: |
FIREBRICK, INSULATING, DENSITY AVG.LB/CU.FT.31 ASTM-C437-61 MELTING POINT 2750F, MODULUS OF RUPTURE PSI 150, (ASTM-C93-67) COLD CRUSHING STRENGTH PSI 145, (ASTM-C93-67) PERMANENT LINEAR CHANGE- MEAN TEMPERATURE AT 2250F PERCENT O, (ASTM-C210-68) THERMAL CONDUCTIVTY, BTU.IN/HR.SQ.FT. DEG.F. MEAN TEMPERATURE AT 2000F, 1.9 (ASTM C-182-71) DEFORMATION UNDER HOT LOAD PER CENT AT 10 PSI. 1-1/2 HR AT 2200F, 0.1 (ASTM-C16-65) CHEMICAL ANALYSIS PER CENT ACCORDING TO ASTM-C573-70, FOR SERVICE TEMPERATURE 2300F BACKUP. NOTE- TO BE PACKED IN SUITABLE CARTONS, MOUNTED ON PALLETS WITH-SUITABLE STRAPPING TO WITHSTAND ROUGH OCEAN FREIGHT HANDLING. * THIRD PARTY INSPECTION IS REQUIRED. THE SCOPE OF WORK FOR TPI IS AS PER ATTACHED SHEET: "TPI - MED - 22-01/98 - REV.1" TYPE THICK WIDTH LENGTH (INCH) (INCH) (INCH) MK-H 3 9 13.1/4 | |
|
|
APPLICATION=FOR HEATERS, FURNACE,STACK |
|
BULK DENSITY=AVERAGE 31 PER ASTM C437-61 |
|
CONDUCTIVITY, THERMAL=1.9 @ MEAN TEMPERATURE OF 2000 DEGF PER ASTM C182-71 |
|
CONTENT, ALUMINUM OXIDE=(Al2O3) 37% PER ASTM C-573 |
|
CONTENT, FERRIC OXIDE=(Fe2O3) 0,7% MAXIMUM |
|
CONTENT, SILICA DIOXIDE=(SiO2)61% PER ASTM C-573 |
|
HEIGHT=3 |
|
LENGTH=13-1/4 |
|
SHAPE=RECTANGULAR MK-H |
|
TEMPERATURE=2300 BACK UP |
|
WIDTH=9 |
|
MODULUS OF RUPTURE=150 PER ASTM C93-67 |
|
PERMANENT LINEAR CHANGE=0 % @ MEAN TEMPERATURE OF 2250 DEGF PER ASTM C210-68 |
|
STRENGTH, COLD CRUSHING=145 PER ASTM C93-67 |
| |
|
2 |
038211 |
REFRACTORY:FORM FIREBRICK INSULATING,6-3/4 IN WD X 9 IN LG X 3 IN THK STRAIGHT |
15600 |
EACH |
|
|
Description: |
FIREBRICK, INSULATING, DENSITY AVG.LB/CU.FT.31 ASTM-C437-61 MELTING POINT 2750F, MODULUS OF RUPTURE PSI 150, (ASTM-C93-67) COLD CRUSHING STRENGTH PSI 145, (ASTM-C93-67) PERMANENT LINEAR CHANGE- MEAN TEMPERATURE AT 2250F PERCENT O, (ASTM-C210-68) THERMAL CONDUCTIVTY, BTU.IN/HR.SQ.FT. DEG.F. MEAN TEMPERATURE AT 2000F, 1.9 (ASTM C-182-71) DEFORMATION UNDER HOT LOAD PER CENT AT 10 PSI. 1-1/2 HR AT 2200F, 0.1 (ASTM-C16-65) CHEMICAL ANALYSIS PER CENT ACCORDING TO ASTM-C573-70, FOR SERVICE TEMPERATURE 2300F BACKUP. NOTE- TO BE PACKED IN SUITABLE CARTONS, MOUNTED ON PALLETS WITH-SUITABLE STRAPPING TO WITHSTAND ROUGH OCEAN FREIGHT HANDLING. * THIRD PARTY INSPECTION IS REQUIRED. THE SCOPE OF WORK FOR TPI IS AS PER ATTACHED SHEET: "TPI - MED - 22-01/98 - REV.1" TYPE THICK WIDTH LENGTH (INCH) (INCH) (INCH) STRAIGHT 3 6.3/4 9 | |
|
|
APPLICATION=FOR HEATERS, FURNACE,STACK |
|
BULK DENSITY=AVERAGE 31 PER ASTM C437-61 |
|
CONDUCTIVITY, THERMAL=1.9 @ MEAN TEMPERATURE OF 2000 DEGF PER ASTM C182-71 |
|
CONTENT, ALUMINUM OXIDE=(Al2O3) 37% |
|
CONTENT, CALCIUM OXIDE=NOT TRACEABLE |
|
CONTENT, FERRIC OXIDE=(Fe2O3) 0,7% MAXIMUM |
|
CONTENT, MAGNESIUM OXIDE=NOT TRACEABLE |
|
CONTENT, SILICA DIOXIDE=(SiO2)61% |
|
FORM=FIREBRICK |
|
HEIGHT=THK 3 |
|
LENGTH=9 |
|
SHAPE=STRAIGHT |
|
TEMPERATURE=2300 BACK UP |
|
WIDTH=6-3/4 |
|
MODULUS OF RUPTURE=150 PER ASTM C93-67 |
|
PERMANENT LINEAR CHANGE=0 % @ MEAN TEMPERATURE OF 2250 DEGF PER ASTM C210-68 |
|
STRENGTH, COLD CRUSHING=145 PER ASTM C93-67 |
| |
Appreciate receiving your CIF Kuwait offer on or before January 03, 2012. |